Effect of Adding SiC on Resistance Wear and Hardness through Stir Casting of Aluminum Matrix Composites

Nur, Wahyuni and Rusdi, Nur and Ilyas, Renreng and Mohammad, Adnan (2018) Effect of Adding SiC on Resistance Wear and Hardness through Stir Casting of Aluminum Matrix Composites. In: International Conference on Engineering, Technology and Industrial Application (ICETIA) 2018, 12-13 Desember 2018, Surakarta, Indonesia. (Submitted)

Archive (Artikel)
Abstract Book ICETIA 2018.pdf

Download (3MB) | Preview
Archive (Peer Review)
Peer Review ICETIA 2018 Nur Wahyuni et al..pdf

Download (977kB) | Preview
Archive (Hasil Turnitin)
Hasil Turnitin Paper 150_Nur_Wahyuni et al..pdf

Download (2MB) | Preview


This study aims to determine the wear resistance and hardness of aluminum matrix composites (AMCs) plus SiC amplifier with a ratio of 98% Al-Si and 2% SiC using the stir casting method. The research method is the wear test with ogoshi high-speed universal wear testing machine and hardness test with the Brinell method. Variation the pouring temperature used in the stir casting method are 688°C, 738°C, and 788°C. The wear test results at abrasion speed of 0,250 m/sec in 60 seconds, shows that the specific wear value of the compressive force is 2.12 kg which tends to be higher when compared to the specific wear value in the compressive force of 3.18 kg and 6.36 kg. Hardness testing results showed that the addition of SiC to aluminum matrix composites (AMCs) showed an increase in the value of matrix hardness. The specimen samples without SiC addition have the lowest hardness level compared to those using the addition of 2% SiC (Silicon Carbide) which is 578.01 HBW 10/3000/15.

Item Type: Conference or Workshop Item (Paper)
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Department of Mechanical Engineering > Teknik Mesin
Depositing User: editor pnup
Date Deposited: 27 Feb 2019 07:18
Last Modified: 26 Mar 2019 11:21
URI: http://repository.poliupg.ac.id/id/eprint/877

Actions (login required)

View Item View Item