Mechanical Properties On Friction Stir Welding of Aluminum Alloy 5052

Rusdi, Nur and Ahmad, Zubair Sultan and Muhammad, Arsyad Suyuti (2017) Mechanical Properties On Friction Stir Welding of Aluminum Alloy 5052. ARPN Journal of Engineering and Applied Sciences, 12 (15). pp. 4445-4450. ISSN 1819-6608

[img] Text (Artikel)
ARPN_JEAS_12_15_2017_Nur et al.pdf

Download (773kB)
[img] Text (Peer Review (update))
Peer Review_ARPN_JEAS_12_8_2017_Nur et al.pdf

Download (3MB)
[img] Text (Cek Plagiasi)
Cek Plagiasi_Nur et al._2017_ ARPN.pdf

Download (211kB)
[img]
Preview
Text
jeas_0817_6229.pdf

Download (311kB) | Preview
Official URL: http://www.arpnjournals.com/jeas/

Abstract

Aluminum alloy was a material widely used in the fields of engineering but not easily connected by the welding process. In this research experiments conducted using friction stir welding (FSW). This study aims to analyze the resulting mechanical properties as well as studying the effect of welding parameters i.e. shoulder diameter, round tool, and speed in welding (feeding) in the friction stir welding on aluminum material AA 5052. The mechanical properties were analyzed include tensile strength and bending strength of results welding. Best mechanical properties are on the tool with a shoulder diameter of 17.8 mm the highest tensile strength at 1300 rpm with a feeding rounds of 50 mm/min at 222.1 MPa and the highest of bending strength at 1300 rpm with a feeding around 208 mm/min at 422.6 MPa, With a smaller shoulder diameter, round and proper feeding friction and forging processes that occur while welding gives smaller influence on the decline in good mechanical properties in the material to be joined.

Item Type: Article
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Department of Mechanical Engineering > Teknik Mesin
Depositing User: Dr Rusdi Nur
Date Deposited: 30 Aug 2017 00:00
Last Modified: 21 Jun 2020 04:08
URI: http://repository.poliupg.ac.id/id/eprint/467

Actions (login required)

View Item View Item